ASTM F562-13 - 1.3.2013
 
1. Scope

1.1 This specification covers requirements of wrought 35cobalt-35nickel-20chromium-10molybdenum alloy (UNS R30035) in the form of bar and wire, used for the manufacture of surgical implants. This alloy depends on combinations of work strengthening and aging to attain a variety of combinations of strength and ductility.

1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.

 
2. Referenced Documents

A751-21

Standard Test Methods and Practices for Chemical Analysis of Steel Products

ISO 5832/6

Implants for Surgery--Metallic Materials Part 6: Wrought cobalt-nickel-chromium-molybdenum Alloy

AMS 2632

Ultrasonic Inspection of Thin Materials

AMS 2630

Inspection, Ultrasonic Product over 0.5 inch (12.7 mm) Thick

AMS?2269

Chemical Check Analysis Limits--Wrought Nickel Alloys and Cobalt Alloys

E8/E8M-24

Standard Test Methods for Tension Testing of Metallic Materials

ISO?9001

Quality Management Systems

E112-13(2021)

Standard Test Methods for Determining Average Grain Size

E354-21e1

Standard Test Methods for Chemical Analysis of High-Temperature, Electrical, Magnetic, and Other Similar Iron, Nickel, and Cobalt Alloys (Includes all amendments and changes 2/23/2022).

F981-23

Standard Practice for Assessment of Muscle and Bone Tissue Responses to Long-Term Implantable Materials Used in Medical Devices

IEEE/ASTM SI 10

American National Standard for Metric Practice

ISO?6892

Metallic Materials--Tensile Testing at Ambient Temperature

E29-22

Standard Practice for Using Significant Digits in Test Data to Determine Conformance with Specifications